The raw materials for the production of optical glass are some oxide, hydroxide, nitrate and carbonate, and the introduction of phosphate or fluoride in accordance with the requirements of the formula. In order to ensure the transparency of the glass, we must strictly control the content of colored impurities, such as iron, chromium, copper, manganese, cobalt, nickel and so on. Accurate weighing, uniform mixing. The main production processes are melting, forming, annealing and inspection.
Smelting with single crucible batch smelting method and tank furnace (see kiln) continuous smelting process. A single crucible melting method can be divided into clay crucible melting method and platinum crucible melting method. No matter what kind of smelting method is used, it is necessary to use a blender to mix, and the temperature and the stirring are controlled strictly, so that the optical glass liquid can reach a high degree of uniformity.
II optical glass forming method for forming a classical broken crucible method, rolling method and casting method. But now, more and more widely by leaking molding (using a single crucible or outflow continuous melting liquid), can directly pull rod or dropping pressure type or leakage material forming the large size of the blank, improve material drop efficiency of yield and usage.
Annealing in order to maximize the elimination of the internal stress of the glass to improve the optical uniformity, we must develop a strict annealing system for precision annealing.
The test indicators are: optical constants, optical uniformity, birefringence, stripes and bubble.
Last one:Glass insulation - how do users choose Next one:The characteristics and applications of optical lenses
Fax:0513-8879-3069
Mobilephone:137-0627-6012
Mailbox:596545997@qq.com / hahuihong@hotmail.com
Address:Liu Wei Qu Shuang Lou industrial zone of Jiangsu County of Haian Province town of 31 groups